Thermo-Mechanical Properties of Alumina Films Created Using the Atomic Layer Deposition Technique

Interdigitated humidity sensors with atomic layer deposited ALD coatings of aluminum oxide demonstrated no leakage current relative to uncoated sensors stored in the ambient, indicating Al2O3 may be used to limit the effects of H2O and other chemical species in miniaturized mechanical- and electronicdevices. The long term durability of such coatings is not known, but may be predicted from the related material characteristics. The modulus and hardness of Al2O3 were therefore measured by nanoindentation using a Berkovich tip. Because the coatings are brittle and possess a significant tensile stress, the influence of film stress on the indentation measurements was quantified using a numerical analysis protocol which also considered the effect of substrate compliance. The film stress and coefficient of thermal expansion for Al2O3 were determined using the wafer curvature method. Film stress was characterized using thermal cycling up to 500 9702C. Separate SiSiO2Si microcantilever arrays demonstrated a stress variation according to the thickness of Al2O3 coatings. Fracture toughness was examined by indentation with a cube-corner tip the estimates are subject to film stress and the material-dependent geometry factor.