Fabrication and Testing of Carbon Fiber/Phenylated Polyquinoxaline Resin Composite,

Santelli, Mary L.

Fabrication and Testing of Carbon Fiber/Phenylated Polyquinoxaline Resin Composite,

Active / Technical Report | Accession Number: ADA309265 |

Open PDF

Abstract:

Techniques were developed for fabricating carbon fiber composites using a Naval Ordnance Laboratory developed high temperature resin, phenylated polyquinoxaline PPQ. Composites with interlaminar shear and flexural strengths about 80 of those for similar epoxy composites were obtained. Heat aging at 343 deg C 650 deg F, in air, revealed excellent initial strength retention at temperature but significant loss of strength after 168 hours.

Author(s):

Santelli, Mary L.

Author Organization(s):

NAVAL ORDNANCE LAB WHITE OAK MD

Pagination:

0048

Security Markings

DOCUMENT & CONTEXTUAL SUMMARY

Distribution:

Approved For Public Release

RECORD

Collection: TR

Identifying Numbers

Report Number(s):

NOLTR-71-187

Monitor Series:

NOLTR

Subject Terms

Joint Capability Areas:

JCA_5_Command and Control; JCA_1_Force Support; JCA_3.2_Engagement; JCA_3_Force Application; JCA_5.2_Understand; JCA_3.2.1_Kinetic Means; JCA_1.3_Human Capital Management; JCA_1.3.2_Personnel Management; JCA_5.3_Planning

Modernization Areas:

Directed Energy

Communities of Interest:

Weapons Technologies

Descriptor(s):

*POLYMERS, *FIBER REINFORCED COMPOSITES, *CARBON FIBERS, TEST AND EVALUATION, TEMPERATURE, AGING(MATERIALS), NAVY, HIGH TEMPERATURE, FABRICATION, RETENTION(GENERAL), FLEXURAL STRENGTH, LOSSES, EPOXY COMPOSITES, HEAT, ORDNANCE LABORATORIES, QUINOXALINES

Field(s)/Group(s):

Polymer Chemistry, Laminates and Composite Materials, Plastics, Mechanics

Keyword(s):

*PHENYLATED, *POLYQUINOXALINE RESIN

Report Date:

1971 Nov 01

Creation Date:

1996 Jun 25