Title:

A Nonlinear Fracture Mechanics Predictive Procedure for the Short Crack Effect in Fatigue,

Descriptive Note:

Corporate Author:

BATTELLE COLUMBUS LABS OH

Report Date:

1982-09-01

Pagination or Media Count:

26.0

Abstract:

When the predictive techniques of linear elastic fracture mechanics LEFM are applied to physically short fatigue cracks, it is often found that the actual crack growth rate is considerably underestimated. This means that damage tolerance and other fracture control methods that rely on accurate crack growth predictions could be quite nonconservative. Consequently, considerable attention has been devoted to identifying the causes of the accelerated growth rates and on ways of improving upon the currently available predictions. Virtually all of these have been based exclusively upon LEFM considerations. In contrast, this paper addresses the short crack problem from the point of view that an elastic-plastic fracture mechanics parameter may offer the basis for a resolution of the dilemma. The specific approach that is taken is one that focusses on the crack-tip crack-opening displacement CTOD as a characterizing parameter. The use of CTOD is at least as general as current LEFM procedures. Of equal importance, the CTOD may possibly be valid where LEFM is not. An illustrative example is used to show the non-linear character of this approach.

Subject Categories:

  • Metallurgy and Metallography
  • Theoretical Mathematics
  • Mechanics

Distribution Statement:

APPROVED FOR PUBLIC RELEASE