Accession Number:

ADA954842

Title:

Development of a Stable-Beta Titanium Alloy.

Descriptive Note:

Quarterly rept. no. 12, 1 Apr-30 Jun 65,

Corporate Author:

TITANIUM METALS CORP OF AMERICA NEW YORK

Personal Author(s):

Report Date:

1965-06-30

Pagination or Media Count:

38.0

Abstract:

Evaluation of four metastable alloys, Ti-8Mo-8V-2Fe-3Al, Ti-8Mo-8V-5Co-3Al, Ti-17V-7.5C0-3A1 and Ti-17V-2Fe-2C0-3Al, stabilized by aging for eight hours at 1100F, showed that although Ti-8Mo-8V-5Co-3Al and Ti-17V-7.5Co-3Al had greater room temperature and 600F strength, their rom temperature notch strengths were inferior to those of Ti-8Mo-8V-2Fe-3Al. Weldability studies indicated that Ti-8Mo-8V-2Fe-3Al combined good ductibility with moderate strength levels 134 Ksi yield when aged for two hours at 900F aging for 6 to 8 hours at 900F produced a yield strength of 150 Ksi with 3 elongation. The mill evaluation of Ti-8Mo-8V-2Fe-3Al proceeded with the evaluation of sections suct from 2-inch and 12-inch thick plate. Excellent strengthductility combinations were obtained from the 12-inch section. Keywords Titanium alloys Molybdenum Vanadium Iron Aluminum Cobalt.

Subject Categories:

  • Metallurgy and Metallography

Distribution Statement:

APPROVED FOR PUBLIC RELEASE