Three-Dimensional Material Properties of Composites with S2-Glass Fibers or Ductile Hybrid Fabric

Descriptive Note:

Journal article

Corporate Author:

LAWRENCE TECHNOLOGICAL UNIV SOUTHFIELD MI

Report Date:

2013-01-13

Pagination or Media Count:

19.0

Abstract:

Material properties were determined for fiber-reinforced polymers FRPs with respect to all three material orientations using existing ASTM standards when applicable. The in-plane and out-of-plane material properties include shear strength, shear modulus, compressive strength, compressive modulus, tensile strength, tensile modulus, and Poissons ratio. Parameters included in this study include the resin and fiber composition, the nominal thickness of the composite plate, and the test temperature. The three material compositions were 1 Huntsman PolyUrethane PU Rencast 6405 with S-2 Glass fibers, 2 Applied Poleramic API SC-15 Epoxy with S-2 Glass fibers, and 3 Huntsman PU Rencast 6405 with Ductile Hybrid Fabric. The nominal thickness were 1.91 cm., 2.54 cm., and 3.81 cm. The nominal test temperatures were -40 deg C, 21 deg C ambient, and 60 deg C.

Subject Categories:

  • Refractory Fibers
  • Laminates and Composite Materials
  • Theoretical Mathematics

Distribution Statement:

APPROVED FOR PUBLIC RELEASE