The Evaluation of the Damping Characteristics of a Hard Coating on Titanium

Descriptive Note:

Master's thesis

Corporate Author:

AIR FORCE INST OF TECH WRIGHT-PATTERSON AFB OH SCHOOL OF ENGINEERING AND MANAGEMENT

Personal Author(s):

Report Date:

2004-03-01

Pagination or Media Count:

116.0

Abstract:

Engine failures due to fatigue have cost the Air Force an estimated 400 million dollars per year over the past two decades Garrison, 2001. Damping treatments capable of reducing the internal stresses of fan and turbine blades to levels where fatigue is less likely to occur have the potential for reducing cost while enhancing reliability. This research evaluates the damping characteristics of magnesium aluminate spinel, MgOAl2O3, mag spinel on titanium plates. The material and aspect ratio were chosen to approximate the low aspect ratio blades found in military gas turbine fans. The plates were tested with a cantilevered boundary condition, using electrodynamics shaker excitation. The effective test area of each specimen was 4-12 in. x 4-12 in. The nominal plate thickness was 18 in. Mag spinel was applied to both sides of the plate, at a thickness of .01 in., and damping tests were run at room temperature. The effect of the coating was evaluated at the 2nd bending mode mode 3 and the chordwise bending mode mode 4. A scanning laser vibrometer revealed the frequency and shape of each mode for the plates. Sine sweeps were used to characterize the damping of the coated and uncoated specimens for the modes tested. The coating increased damping nonlinearly for both modes tested. The test results are presented in this document.

Subject Categories:

  • Metallurgy and Metallography
  • Fluid Mechanics
  • Mechanics

Distribution Statement:

APPROVED FOR PUBLIC RELEASE