Mechanical Properties of Neat Polymer Matrix Materials and Their Unidirectional Carbon Fiber-Reinforced Composites.

Descriptive Note:

Contract rept. May 84-May 85,

Corporate Author:

WYOMING UNIV LARAMIE

Report Date:

1988-12-01

Pagination or Media Count:

213.0

Abstract:

The mechanical properties of two neat resin systems for use in carbon fiberepoxy composites were characterized. This included tensile and shear stiffnesses and strengths, coefficients of thermal and moisture expansion, and fracture toughness. Tests were conducted on specimens in the dry and moisture-saturated states, at temperatures of 23 deg C, 82 deg C, and 121 deg C. The neat resins tested were American Cyanamid 1806 and Union Carbide ERX-4901BMPDA. Results were compared to previously tested neat resins. Four unidirectional carbon fiber-reinforced composites were mechanically characterized. Axial and transverse tension and in-plane shear strengths and stiffnesses were measured, as well as transverse coefficients of thermal and moisture expansion. Tests were conducted on dry specimens only at 23 deg C and 100 deg C. The materials tested were AS43502, AS65245-C, T300BP907, and 060001806 unidirectional composites. Scanning electron microscopic examination of fracture surfaces was performed to permit the correlation of observed failure modes with the environmental test conditions.

Subject Categories:

  • Polymer Chemistry
  • Laminates and Composite Materials
  • Plastics
  • Mechanics

Distribution Statement:

APPROVED FOR PUBLIC RELEASE