Corrosion of Aircraft Materials: Correlation Between Nanometer Scale and Macroscopic Structural Damage Parameters
LYNNTECH INC COLLEGE STATION TX
Pagination or Media Count:
The following work has been carried out during the reporting period 1 imaging of pitting corrosion initiation in aluminum at the nanometer scale, 2 study of the effects of main atmospheric pollutants on the initiation of the corrosion process 3 identification of surface regions at an aluminum sample where corrosion is most likely to occur 4 measurements of the electrochemical impedance spectra on Al sample before and during the pitting process in NaCl 5 identification of the impedance parameters characteristic for the pitting the corrosion of the aluminum sample.