Morphology of Highly Textured Polyethylene/Polyethylene-Propylene Semicrystalline Diblock Copolymers

Descriptive Note:

Technical rept.,

Corporate Author:

MASSACHUSETTS INST OF TECH CAMBRIDGE DEPT OF CHEMICAL ENGINEERING

Personal Author(s):

Report Date:

1993-12-03

Pagination or Media Count:

42.0

Abstract:

A series of semicrystalline diblock copolymers of polyethylene polyethylenepropylene EEP were subjected to high levels of plane strain compression using a channel die. Deformations were imposed both below and above the melting point of the E block. The crystallographic and morphological textures were examined using wide-angle X-ray diffraction pole figure analysis and two dimensional small-angle X-ray scattering. The lattice unit cell orientation of the crystallized E chains with respect to the lamellar superstructure was determined, as well as the lamellar orientation relative to the specimen boundaries. When the diblocks are textured above the E block melting point at various compression ratios, the lamellae orient perpendicular to the plane of shear, while texturing below T, causes the lamellae to orient parallel to the plane of shear. The orientation of the crystallized E chains was perpendicular to the lamellar normal, irrespective of the texturing temperature. Semicrystalline polymers, Diblock copolymers.

Subject Categories:

  • Polymer Chemistry
  • Plastics
  • Crystallography
  • Nuclear Physics and Elementary Particle Physics

Distribution Statement:

APPROVED FOR PUBLIC RELEASE