Accession Number:

ADA160443

Title:

Thermal Stability of Certain Hydrated Phases in Systems Made Using Portland Cement.

Descriptive Note:

Final rept.,

Corporate Author:

ARMY ENGINEER WATERWAYS EXPERIMENT STATION VICKSBURG MS STRUCTURES LAB

Personal Author(s):

Report Date:

1985-08-01

Pagination or Media Count:

79.0

Abstract:

As part of the study of hydraulic-cement system for use in possible underground isolation of nuclear wastes, this study was made to determine the temperature stability of ettringite and chloroaluminate. Either or both of these phases may be expected in a hydraulic cement system depending on the presence of salt. NaCl. The study of ettringite was made using 15 mixtures that contained portland cement, plaster, 2 levels of water, and in some mixtures, 1 of 6 pozzolans 3 fly ashes, 1 slag, a silica fume, a natural pozzolan, plus a 16th mixture with anhydrous sodium sulfate replacing plaster CaSO4 . 12H20. Specimens were made and stored at 23, 50, and 75 C or 23, 75, and 100 C all four temperatures in one case for periodic examination by x-ray diffraction for phase compositiion and ettringite stability, and testing for compressive strength and restrained expansion. A more limited study of the stability of chloroaluminate was made along the same lines using fewer mixtures, salt instead of plaster, and higher temperatures plus some pressure. It was found that while some ettringette was decomposed at 75 C, depending on the composition of the mixture, all ettringite was undetectable by X-ray diffraction at 100 C, usually within a few days. The evidence indicates that the ettringite became amorphous and no significant test phases formed in its place. Since there was no corresponding loss in strength or reduction in volume, this loss of ettringite crystallinity was considered to be damaging. Based on much more limited data, chloroaluminate was found to decompose between 130 C at 25 psi and 170 C at 100 psi no significant phases replaced it.

Subject Categories:

  • Ceramics, Refractories and Glass
  • Construction Equipment, Materials and Supplies
  • Thermodynamics