Corrosion Fatigue Crack Growth Rates of Weldments in Q1N Steel,

Descriptive Note:

Corporate Author:

ADMIRALTY MARINE TECHNOLOGY ESTABLISHMENT POOLE (ENGLAND)

Personal Author(s):

Report Date:

1983-06-01

Pagination or Media Count:

33.0

Abstract:

Low frequency fatigue crack growth rates in air and seawater are reported for manual metal arc, synergic metal inert gas, electron beam and laser beam welds in Q1N steel. The stress corrosion crack growth susceptibility in seawater of the weldments was also studied and both the electron beam and laser beam welds exhibited susceptibility whilst the other welds and parent steel did not. All welds except the as-welded laser beam welds showed silmilar fatigue crack growth rates to the parent plate. When tested in seawater the laser beam weld was found to exhibit exceptionally fast crack growth rates. The factors influencing fatigue crack growth in weldments are discussed. Author

Subject Categories:

  • Properties of Metals and Alloys
  • Fabrication Metallurgy
  • Marine Engineering
  • Mechanics

Distribution Statement:

APPROVED FOR PUBLIC RELEASE