The Influence of Environment on Crack Behavior.
MARTIN MARIETTA AEROSPACE DENVER COLO DENVER DIV
Pagination or Media Count:
The analytical expressions presented in this report relate the crack velocity and the failure time to the surface-layer stress coefficient for compact-tension specimens of Ti6Al-4V and a 4130 steel subjected to stress-corrosion cracking. The experimental data for the threshold stress intensity factor and the crack velocities for various stress intensity factors agree well with the calculated values. Author