OBSERVATIONS OF DISLOCATIONS IN CAWO4 BY TRANSMISSION ELECTRON MICROSCOPY.

Descriptive Note:

Technical rept.,

Corporate Author:

HONEYWELL RESEARCH CENTER HOPKINS MINN

Personal Author(s):

Report Date:

1965-07-01

Pagination or Media Count:

1.0

Abstract:

The distribution of dislocations in deformed calcium tungstate was studied by electron transmission microscopy. The photomicrographs confirmed earlier optical observations that 001 100 is the slip system of this material between 500 - 900C. Screw dislocations, long edge dislocation dipoles, quadrupoles and tangles of dislocations were observed in foils prepared from specimens deformed at 500C. Specimens deformed at 700C showed similar features, except that many of the long dipoles had split into long strings of prismatic loops. At 900C the loops were more isolated and sometimes grew to a diameter exceeding the thickness of the foil. Many single dislocations could also be seen with nearly pure edge or screw orientation. Two models are proposed for quadrupole formation and their relative stability considered. Strain hardening is thought to be due to the interaction of dislocations with multipoles and prismatic circular loops. Author

Subject Categories:

Distribution Statement:

APPROVED FOR PUBLIC RELEASE