FAULTING IN SODIUM AZIDE
MARTIN MARIETTA CORP BALTIMORE MD RESEARCH INST FOR ADVANCED STUDIES
Pagination or Media Count:
This report includes Measurement of stacking fault probabilities in bulk specimens by Henry M. Otte, D. O. Welch and G. F. Bolling. In x-ray diffraction measurements of NaN3 it has been noted that after deformation, the line broadening was consistent with that expected from formation of deformation stacking faults. However, the anticipated shifts in the peak positions could not be detected. An explanation for this is suggested on the basis of the supposition that 1 extrinsic stacking faults are at least as likely to form in NaN3 as intrinsic stacking faults and 2 x-ray diffraction analysis for extrinsic stacking faults is applicable.