RECRYSTALLIZATION OF COLD DEFORMED TUNGSTEN
FOREIGN TECHNOLOGY DIV WRIGHT-PATTERSON AFB OH
Pagination or Media Count:
An investigation of the recrystallization of cold deformed W is described. Electronic microphotographs were made of undeformed and deformed test specimens. Hardness tests were made on deformed specimens subjected to various vacuum annealing temperatures from 800 to 1650 degrees. X-ray diffraction studies were made on undeformed, deformed, and annealed test pieces the relation of the broadening of the spectral line 321 to the annealing temperature was established.
- Properties of Metals and Alloys