Accession Number : ADA171743
Title : Environmental Effects on Impact Damage Tolerance of Hybrid Composite Material
Descriptive Note : Final rept.
Corporate Author : NAVAL ACADEMY ANNAPOLIS MD
Personal Author(s) : Wood, Lawrence E
Report Date : 28 May 1986
Pagination or Media Count : 56
Abstract : The behavior of an intraply hybrid composite material of polyethylene and graphite fibers in an epoxy matrix under the effects of environmental conditioning, impact damage, and fatigue loading was investigated. Although the ultimate tensile strength of the hybrid material was found to be lower than that of graphite material alone, the specific strengths of the materials were comparable. Dye-penetrant enhanced X-ray radiography and edge replication were used to evaluate the damage growth of the test material. Impact damage evaluations showed the initial crack tolerance of the hybrid materials was better than that of conventional graphite. Specimens of both materials were soaked in standard ocean water and their moisture absorption observed. The moisture absorption percentages for the hybrid and graphite materials were 2.91 percent and 1.47 percent by weight respectively. Both dry and wet hybrid material was subjected to impact and fatigue loading. During fatigue loading the hybrid material exhibited viscoelastic behavior characterized by a non-linear loading curve. The wet hybrid material experienced both a sharper reduction in stiffness, and a greater increase in damage area than the dry material.
Descriptors : *GRAPHITED MATERIALS , *HYBRID SYSTEMS , *DAMAGE ASSESSMENT , GROWTH(GENERAL) , CRACKS , CARBON FIBERS , X RAYS , ULTRASONICS , EPOXY LAMINATES , NAVAL RESEARCH , ABSORPTION , MOISTURE , EPOXY RESINS , RADIOGRAPHY , STATIC TESTS , COMPOSITE MATERIALS , POLYETHYLENE , TENSILE STRENGTH , IMPACT
Subject Categories : Laminates and Composite Materials
Solid State Physics
Distribution Statement : APPROVED FOR PUBLIC RELEASE