Accession Number : AD0824852
Title : STRESS CORROSION SUSCEPTIBILITY OF WELDED ALUMINUM ALLOYS.
Descriptive Note : Final rept. Jul 66-Aug 67,
Corporate Author : DOUGLAS AIRCRAFT CO LONG BEACH CA AIRCRAFT DIV
Personal Author(s) : Turley, Richard F. ; Avery, Charles H. ; Dash, Edward
Report Date : AUG 1967
Pagination or Media Count : 173
Abstract : The program determined threshold stress levels for 2014-T6, X2021-T8E31, 2024-T81, 2219-T87, X7002-T6, 7039-T64, and 7106-T6. Variables were sheet and plate, long transverse grain direction, welded and post-weld heat treated, notched and unnotched. Tests were conducted using step load and constant load 500 hours alternate immersion in synthetic sea water at sustained stress levels up to 75-percent yield strength. All basic, unwelded alloys, sheet and plate, had thresholds above 75-percent yield strength. Thresholds for unnotched sheet alloys were below 75-percent yield strength for 2014-T6, as welded (W), weld + age (A) and weld + solution heat treat + age (S), X2021-T8E31 (W), 2024-T81 (W), 2219-T87 (S), 7039-T64 (S) and 7106-T6 (A) (S). The most susceptible to stress corrosion cracking was X2021-T8E31 (W). A fatigue crack at the edge of the weld bead caused increased susceptibility to stress corrosion for several of the sheet alloy-weld-tempers. For unnotched plate product, stress corrosion cracking was incurred for only 2014-T6 (S) and 7039-T64 (S) below 75-percent yield strength; this was at higher stress levels than the (W) and (A) tempers tested. A fatigue crack at the edge of the weld bead caused severe susceptibility to stress corrosion cracking for plate alloys, X-2021-T8E31 (S), 7039-T64 (S) and 2014-T6 (S). An Engineering Data Materials Matrix is presented. Stress corrosion cracking typically initiated at the edge of the weld bead and progressed along the fusion line branching into the weld bead and heat affected zone. (Author)
Descriptors : *STRESS CORROSION), (*ALUMINUM ALLOYS, WELDS, CRACKS, SHEETS, METAL PLATES, SEA WATER, LIQUID IMMERSION TESTS, HEAT TREATMENT, FRACTURE(MECHANICS).
Subject Categories : PROPERTIES OF METALS AND ALLOYS
Distribution Statement : APPROVED FOR PUBLIC RELEASE