Title :   CAUSES OF CRACKING IN HIGH-STRENGTH WELD METALS


Descriptive Note : Rept. for 15 Nov 1954-15 Nov 1955


Corporate Author : BATTELLE MEMORIAL INST COLUMBUS OH


Personal Author(s) : Lowe Jr , A L ; Sopher, R P ; Rieppel, P J


Full Text : https://apps.dtic.mil/dtic/tr/fulltext/u2/093335.pdf


Report Date : Nov 1955


Pagination or Media Count : 41


Abstract : This report summarizes the experimental work in a study to determine the causes of cracking in high-strength weld metals. A new hot-tension machine was designed and built to facilitate the testing of SAE 4340 weld metals on cooling from the molten state. The tests were conducted over the temperature range from 2600 F to 100 F. Results from the studies showed phosphorus to be detrimental to weld-metal cracking resistance. As the phosphorus was increased the ductility was lowered at temperatures near the solidus. Nitrogen content within the normal range of SAE 4340 steels appeared to have little influence on the cracking resistance of the weld deposits. Rare-earth metal additions improved the hot ductility and hot-cracking resistance of the weld metals. An increase in silicon lowered the hot ductility and hot-cracking resistance slightly.


Descriptors :   *METALS , *WELDS , HIGH TEMPERATURE , CRACKING(FRACTURING) , WELD METAL , SURFACE PROPERTIES , HIGH STRENGTH , DUCTILITY , RARE EARTH COMPOUNDS , PHOSPHORUS , CRAZING


Subject Categories : Fabrication Metallurgy